陳 濤１,趙路遠１,李 慧１,黃 ?。?２,吳玉程１,２
(合肥工業(yè)大學(xué)１．材料科學(xué)與工程學(xué)院;２．安徽省有色金屬材料與加工工程實驗室,合肥 ２３０００９)
摘 要:在不同應(yīng)力幅下(６０％σs,７０％σs,８０％σs,９０％σs,σs 為試驗合金屈服強度)對 ７０７５ＧT６５１鋁合金進行了應(yīng)力控制下的疲勞試驗,研究了其循環(huán)應(yīng)變響應(yīng),觀察了疲勞斷口形貌、表面損傷形貌以及顯微組織,分析了疲勞裂紋的萌生及擴展機制.結(jié)果表明:試驗合金中析出了微米級的Al７Cu２Fe顆粒、納米級的η′(MgZn２)相和尺寸較大η(MgZn２)相,此外,還存在尺寸為３~１０nm的細小球狀 GP區(qū);在較高應(yīng)力幅(８０％σs,９０％σs)控制下,試驗合金表現(xiàn)出先軟化后硬化直至斷裂的疲勞行為,而在較低應(yīng)力幅(６０％σs,７０％σs)下則先軟化后明顯硬化并趨于穩(wěn)定;試驗合金主要發(fā)生微孔聚集韌窩型斷裂,在較高應(yīng)力幅下,裂紋源位于粗大夾雜物 Al７Cu２Fe和第二相 MgZn２ 處,位錯大量纏結(jié),而在低應(yīng)力幅下,裂紋源位于基體輕微撕裂處,位錯形態(tài)為分散的短或長直位錯線.
關(guān)鍵詞:７０７５ＧT６５１鋁合金;顯微組織;疲勞斷裂行為
中圖分類號:TG１３ 文獻標志碼:A 文章編號:１０００Ｇ３７３８(２０１７)０７Ｇ０００１Ｇ０５
FatigueFractureBehaviorof７０７５ＧT６５１AluminumAlloyunderStressControl
CHENTao１,ZHAOLuyuan１,LIHui１,HUANGJun１,２,WUYucheng１,２
(１．DepartmentofMaterialsScienceandEngineering;２．AnhuiEngineeringLaboratoryofNonＧferrousMetalsandProcessing,HefeiUniversityofTechnology,Hefei２３０００９,China)
Abstract:Stresscontrolledfatiguetestsatdifferentstressamplitudes,６０％,７０％,８０％ and９０％ ofyield
strength(σs)ofthetestedalloy,respectively,wereconductedon７０７５ＧT６５１aluminum alloy．Thecyclicstrain
responseofthealloywasstudied,thefatiguefracturemorphology,surfacedamagemorphologyandmicrostructure
wereobservedandtheinitiationandpropagationmechanismsoffatiguecrackwereanalyzed．Theresultsshowthat
microＧscaleAl７Cu２Feparticles,nanoＧscaleη′ (MgZn２ )phaseandrelativelylargesizedη (MgZn２ )phasewere
precipitatedinthetestedalloy．Moreover,fineandsphereＧlikeGPzoneswithsizeof３－１０nm wereobserved．
Underthecontrolofrelativelyhighstressamplitude(８０％σs,９０％σs),thetestedalloyshowedafatiguebehaviorof
firstsofteningthenhardeninguntilfracture,whilefirstsofteningthenhardeninguntilbecomingstablerelativelyat
lowstressamplitudes(６０％σs,７０％σs)．Thetestedalloymainlyfracturedinamicroporegathereddimplemanner．
Athighstressamplitude,fatiguecracksinitiatedatthecoarseinclusionofAl７Cu２FeandsecondphaseofMgZn２,
withdislocationtanglingalot．Whereasatlowstressamplitude,thecracksourcewasattheslightlytornpositionof
thesubstrate,andtheproduceddislocationshowedshapesofdispersedshortorlongstraightdislocationlines．
Keywords:７０７５ＧT６５１aluminumalloy;microstructure;fatiguefracturebehavior
陳 濤１,趙路遠１,李 慧１,黃 ?。?２,吳玉程１,２
(合肥工業(yè)大學(xué)１．材料科學(xué)與工程學(xué)院;２．安徽省有色金屬材料與加工工程實驗室,合肥 ２３０００９)
摘 要:在不同應(yīng)力幅下(６０％σs,７０％σs,８０％σs,９０％σs,σs 為試驗合金屈服強度)對 ７０７５ＧT６５１鋁合金進行了應(yīng)力控制下的疲勞試驗,研究了其循環(huán)應(yīng)變響應(yīng),觀察了疲勞斷口形貌、表面損傷形貌以及顯微組織,分析了疲勞裂紋的萌生及擴展機制.結(jié)果表明:試驗合金中析出了微米級的Al７Cu２Fe顆粒、納米級的η′(MgZn２)相和尺寸較大η(MgZn２)相,此外,還存在尺寸為３~１０nm的細小球狀 GP區(qū);在較高應(yīng)力幅(８０％σs,９０％σs)控制下,試驗合金表現(xiàn)出先軟化后硬化直至斷裂的疲勞行為,而在較低應(yīng)力幅(６０％σs,７０％σs)下則先軟化后明顯硬化并趨于穩(wěn)定;試驗合金主要發(fā)生微孔聚集韌窩型斷裂,在較高應(yīng)力幅下,裂紋源位于粗大夾雜物 Al７Cu２Fe和第二相 MgZn２ 處,位錯大量纏結(jié),而在低應(yīng)力幅下,裂紋源位于基體輕微撕裂處,位錯形態(tài)為分散的短或長直位錯線.關(guān)鍵詞:７０７５ＧT６５１鋁合金;顯微組織;疲勞斷裂行為
中圖分類號:TG１３ 文獻標志碼:A 文章編號:１０００Ｇ３７３８(２０１７)０７Ｇ０００１Ｇ０５
FatigueFractureBehaviorof７０７５ＧT６５１AluminumAlloyunderStressControl
CHENTao１,ZHAOLuyuan１,LIHui１,HUANGJun１,２,WUYucheng
１,２
(１．DepartmentofMaterialsScienceandEngineering;２．AnhuiEngineeringLaboratoryofNonＧferrousMetalsandProcessing,
HefeiUniversityofTechnology,Hefei２３０００９,China)
Abstract:Stresscontrolledfatiguetestsatdifferentstressamplitudes,６０％,７０％,８０％ and９０％ ofyield
strength(σs)ofthetestedalloy,respectively,wereconductedon７０７５ＧT６５１aluminum alloy．Thecyclicstrain
responseofthealloywasstudied,thefatiguefracturemorphology,surfacedamagemorphologyandmicrostructure
wereobservedandtheinitiationandpropagationmechanismsoffatiguecrackwereanalyzed．Theresultsshowthat
microＧscaleAl７Cu２Feparticles,nanoＧscaleη′ (MgZn２ )phaseandrelativelylargesizedη (MgZn２ )phasewere
precipitatedinthetestedalloy．Moreover,fineandsphereＧlikeGPzoneswithsizeof３－１０nm wereobserved．
Underthecontrolofrelativelyhighstressamplitude(８０％σs,９０％σs),thetestedalloyshowedafatiguebehaviorof
firstsofteningthenhardeninguntilfracture,whilefirstsofteningthenhardeninguntilbecomingstablerelativelyat
lowstressamplitudes(６０％σs,７０％σs)．Thetestedalloymainlyfracturedinamicroporegathereddimplemanner．
Athighstressamplitude,fatiguecracksinitiatedatthecoarseinclusionofAl７Cu２FeandsecondphaseofMgZn２,
withdislocationtanglingalot．Whereasatlowstressamplitude,thecracksourcewasattheslightlytornpositionof
thesubstrate,andtheproduceddislocationshowedshapesofdispersedshortorlongstraightdislocationlines．
Keywords:７０７５ＧT６５１aluminumalloy;microstructure;fatiguefracturebehavior
FatigueFractureBehaviorof７０７５ＧT６５１AluminumAlloyunderStressControl
CHENTao１,ZHAOLuyuan１,LIHui１,HUANGJun１,２,WUYucheng
１,２
(１．DepartmentofMaterialsScienceandEngineering;２．AnhuiEngineeringLaboratoryofNonＧferrousMetalsandProcessing,
HefeiUniversityofTechnology,Hefei２３０００９,China)
Abstract:Stresscontrolledfatiguetestsatdifferentstressamplitudes,６０％,７０％,８０％ and９０％ ofyield
strength(σs)ofthetestedalloy,respectively,wereconductedon７０７５ＧT６５１aluminum alloy．Thecyclicstrain
responseofthealloywasstudied,thefatiguefracturemorphology,surfacedamagemorphologyandmicrostructure
wereobservedandtheinitiationandpropagationmechanismsoffatiguecrackwereanalyzed．Theresultsshowthat
microＧscaleAl７Cu２Feparticles,nanoＧscaleη′ (MgZn２ )phaseandrelativelylargesizedη (MgZn２ )phasewere
precipitatedinthetestedalloy．Moreover,fineandsphereＧlikeGPzoneswithsizeof３－１０nm wereobserved．
Underthecontrolofrelativelyhighstressamplitude(８０％σs,９０％σs),thetestedalloyshowedafatiguebehaviorof
firstsofteningthenhardeninguntilfracture,whilefirstsofteningthenhardeninguntilbecomingstablerelativelyat
lowstressamplitudes(６０％σs,７０％σs)．Thetestedalloymainlyfracturedinamicroporegathereddimplemanner．
Athighstressamplitude,fatiguecracksinitiatedatthecoarseinclusionofAl７Cu２FeandsecondphaseofMgZn２,
withdislocationtanglingalot．Whereasatlowstressamplitude,thecracksourcewasattheslightlytornpositionof
thesubstrate,andtheproduceddislocationshowedshapesofdispersedshortorlongstraightdislocationlines．
Keywords:７０７５ＧT６５１aluminumalloy;microstructure;fatiguefracturebehavior
０ 引 言
AlＧZnＧMgＧCu系合金因具有比強度高、耐腐蝕性能和熱加工性能好等優(yōu)點,被廣泛用于制造飛機、船舶、汽車及鐵路車輛等的結(jié)構(gòu)件[１Ｇ６],在這些結(jié)構(gòu)件 的 斷 裂 失 效 中 疲 勞 失 效 占 ５０％ ~９０％[７].MERATI等[８]研究了７０７５ＧT６和７０７９ＧT６鋁合金疲勞性能和顯微組織的關(guān)系,發(fā)現(xiàn)在循環(huán)載荷作用下疲勞裂紋易萌生于粗大的第二相顆粒處,并在位錯塞積作用下顆粒自身發(fā)生斷裂或與基體脫黏導(dǎo)致微裂紋產(chǎn)生.周昆等[９]發(fā)現(xiàn)７０７５ＧRRA 鋁合金的低周疲勞裂紋主要萌生于滑移帶,或者析出物與基體交界處.然而材料的疲勞斷裂既與其加載條件有關(guān),又受其顯微組織影響,為了探究這三者之間的關(guān)系,作者選用 T６５１熱處理的７０７５鋁合金(一種具有代表性的 AlＧZnＧMgＧCu系合金),在應(yīng)力控制下對其進行了疲勞試驗,觀察了疲勞斷口形貌和顯微組織,分析了疲勞斷裂行為,以期對該合金顯微組織和性能有更全面的認識,為該合金的應(yīng)用提供可靠依據(jù).
１ 試樣制備與試驗方法
試驗用７０７５鋁合金由西南鋁業(yè)提供,其化學(xué)成分如表１所示.先將該合金坯料加熱至４２０℃,再用１２５００t擠壓機擠壓成尺寸為１１０mm×１３０mm×２３０mm 的塊狀鑄錠;將鑄錠加熱至４７０ ℃保溫２h后水淬,隨后進行１２０ ℃×２４h的時效處理(水淬),最后 進 行 預(yù) 拉 伸(變 形 量 ２％),得 到 試 驗 用 ７０７５ＧT６５１鋁合金.
根據(jù) GB/T２２８－２００２,在試驗合金上加工出?８mm×４０ mm 的拉 伸 試 樣,在 MTSLandmark２５０KN 型電液伺服試驗機上進行靜載拉伸試驗,拉伸速度為２mm??min－１,測得其抗拉強度σb、屈服強度σs、伸長率 A、斷面收縮率 Z 分別為 ５２９ MPa,４５０MPa,１０％,６．８％.根據(jù) GB/T４３３７－２００８,將 試 驗 合 金 加 工 成?６．５mm×２８mm 的疲勞試樣,利用 MTSLandmark２５０KN 型電液伺服試驗機在室溫下進行應(yīng)力控制下的疲 勞 試 驗,采 用 正 弦 波 加 載,應(yīng) 力 幅 分 別 為６０％σs,７０％σs,８０％σs,９０％σs,頻率為２５Hz,應(yīng)力比為０．５.用SU８０２０型場發(fā)射掃描 電 鏡(SEM)和JEMＧ２１００F型場發(fā)射透射電鏡(TEM)觀察試驗合金的顯微組織,并用SEM 附帶的能譜儀(EDS)測析出相成分.此外,還用上述掃描電鏡和透射電鏡分別觀察了疲勞斷口、表面損傷形貌以及疲勞試驗后試樣的位錯組態(tài).透射電鏡試樣先機械減薄至８０μm 左右,再在TenupolＧ５型電解雙噴儀上進行雙噴,雙噴時的電壓為１５~２０V,溫度為－２５ ℃,液氮冷卻,雙噴液為３０％硝酸＋７０％甲醇(體積分數(shù))混合溶液.
２ 試驗結(jié)果與討論
２．１ 顯微組織
７０７５鋁合金是一種典型的可時效強化型高強鋁合金,其時效強化相析出順序為 α相(過飽和固溶體)、GP區(qū)、η′(MgZn２)相 和 η(MgZn２)相.GP區(qū)為與基體完全共格的溶質(zhì)原子偏聚區(qū),η′相為與基體半共格的亞穩(wěn)析出相,η相為與基體非共格的平衡析出相[１０Ｇ１２].由圖１可見:７０７５ＧT６５１鋁合金的顯微組織中存在大量微米級無規(guī)則形狀的粗大分析出相,析出相主要沿軋制方向分布于晶界處;這些粗大析出 相 與 基 體 界 面 處 出 現(xiàn) 明 顯 孔 洞,疑 似因腐蝕所致,孔 洞 的 存 在 使 得 這 些 析 出 相 顆 粒 易剝落;粗大析出相中的鋁、銅、鐵元素含量較高,應(yīng)為 Al７Cu２Fe相[１３Ｇ１５].由圖２可知,７０７５ＧT６５１鋁合金晶內(nèi)或晶界處析出大量長約１００nm、寬約２０nm 的橢球狀或片狀η′強化相以及少量較大的板條狀η相,同時基體中還存在大量尺寸為３~１０nm 的細小球狀GP區(qū).
２．２ 循環(huán)應(yīng)變響應(yīng)
圖３中的應(yīng)變范圍為每個循環(huán)周次中的最大和最小應(yīng)變之差.由圖３可以看出:７０７５ＧT６５１鋁合金在不同應(yīng)力幅下有不同循環(huán)應(yīng)變響應(yīng),但無論應(yīng)力高低,在初始循環(huán)周次條件下,應(yīng)變范圍均隨循環(huán)周次的增加明顯增大,即出現(xiàn)了顯著的軟化現(xiàn)象;在高應(yīng)力幅(９０％σs,８０％σs)下,試驗合金軟化至應(yīng)變范圍最大值后持續(xù)硬化直至斷裂失效;而在低應(yīng)力幅
(７０％σs,６０％σs)下,合金在最初軟化后明顯硬化隨之趨于穩(wěn)定.這種短期且明顯的循環(huán)軟化響應(yīng)與塑性變形在循環(huán)初期的快速積累直接相關(guān),而緩慢且長期循環(huán)硬化穩(wěn)定階段與合金原始顯微組織、粒子與位錯交互作用、位錯的增殖與湮滅等位錯密度動態(tài)變化相關(guān).
２．３ 疲勞斷口形貌
對７０７５ＧT６５１ 鋁合金在不同應(yīng)變幅下進行疲勞試驗,觀察其斷口形貌發(fā)現(xiàn):斷口高低不平且在瞬斷區(qū)有大量的韌窩,因此其主要斷裂方式為微孔聚集韌窩型斷裂;高應(yīng)力幅(９０％σs,８０％σs)下的疲勞斷口特征極為相似,只是應(yīng)力幅越大,疲勞裂紋的萌生區(qū)和擴展區(qū)所占比例越小,疲勞裂紋擴展速率越大.以８０％σs 應(yīng)力幅作用下的疲勞斷口為例進行分析.由圖４可見:斷口疲勞裂紋源周圍存在顯著的放射線特征,這是裂紋在尖端應(yīng)力場作用下因阻力不同而發(fā)生偏轉(zhuǎn),沿一系列存在高度差的宏觀平面向周圍擴展,形成不同斷裂面并相交而成的;斷口局部區(qū)域出現(xiàn)了犁溝、凹陷、疲勞臺階、疲勞條帶和二次裂紋等,這些疲勞條帶彼此平行,其法線方向為裂紋擴展 方 向,且 間 距 隨 著 裂 紋 的 擴 展 而 單 調(diào) 遞增[１６Ｇ１７];斷口處存在大量韌窩或孔洞.在循環(huán)應(yīng)力作用下,合金中的位錯大量增殖且因劇烈滑移發(fā)生堆積,導(dǎo)致脆性富鐵相發(fā)生破裂或與基體脫離而形成許多微小孔洞,或在變形較大的區(qū)域于 MgZn２ 相處產(chǎn)生許多顯微孔洞.這些孔洞在外力的作用下不斷長大、聚集、橋接在一起形成裂紋并不斷擴展,最終形成韌窩或孔洞.富鐵相的脫離還導(dǎo)致韌窩或孔洞周圍存在著大量的解理臺階,降低了合金的疲勞性能.此外,合金中彌散分布的大量第二相使裂紋擴展時受到的阻力增大,裂紋與晶界交匯時使晶粒變形,導(dǎo)致部分晶粒片層斷裂,這些結(jié)果與他人研究結(jié)果相似[１８Ｇ１９].
２．４ 表面疲勞損傷形貌
由圖５可以看出:在較低應(yīng)力幅(６０％σs)循環(huán)作用下,７０７５ＧT６５１鋁合金試樣表面出現(xiàn)了大量垂直于加載方向的微裂紋,這種現(xiàn)象在７０％σs 應(yīng)力幅下同樣可觀察到(圖略);表面基體上有粗大顆粒析出,其EDS譜顯示該顆粒為 Al７Cu２Fe;在８０％σs 應(yīng)力幅循環(huán)作用后,試樣表面的粗大顆粒開裂或者與基體脫黏,這一現(xiàn)象在９０％σs 應(yīng)力幅下更為明顯(圖略).